Thermal stability of a laser-clad NiCrBSi coating hardened by frictional finishing

Abstract

Frictional treatment decreases surface roughness of a NiCrBSi laser coating and increases its microhardness and abrasive wear resistance. Even after softening annealing at 900 °C, the coating subjected to frictional treatment preserves its advantage in hardness and wear resistance over the original clad coating. Annealing at 1000 °C after frictional treatment ensures less effective growth of the hardness and wear resistance of the coating as compared to annealing of the undeformed coating due to the limited precipitation of large Cr23C6 carbides on the deformed surface, which form a wear-resistant framework. © 2017 Author(s).