Structure and luminescent properties of Cs2Sr(VO3)(4): Mn2+

Abstract

We have developed a procedure for thermally stimulated synthesis of a cesium strontium metavanadate, Cs 2Sr(VO 3) 4:Mn 2+ (0.01, 0.50, 1.00, 5.00 at % Mn 2+), using MnO-containing starting mixtures. The EPR spectrum of the material containing 0.01 at % Mn 2+ shows a hyperfine structure due to the incorporation of a small amount of manganese into the diamagnetic double metavanadate host. The luminescent and optical properties of Cs 2Sr(VO 3) 4:Mn 2+ depend on manganese content. In contrast to higher doping levels, doping with 0.01 at % Mn 2+ increases the integrated emission intensity of the vanadate by 10% and improves its chromaticity characteristics (approaching them to those of white light). We assume that this is due to the reduction in the density of vacancy-type growth defects, such as oxygen vacancies. © Pleiades Publishing, Ltd., 2012.