Tungsten (VI) oxide reinforced antimony glasses for radiation safety applications: A throughout investigation for determination of radiation shielding properties and transmission factors

Abstract

We report the functional assessment of tungsten (VI) oxide on gamma-ray attenuation properties of 60Sb2O3-(40-x)NaPO3-xWO3 antimony glasses. The elemental mass-fractions and glass-densities of each glass sample are specified separately for the MCNPX Monte Carlo code. In addition to fundamental gamma absorption properties, Transmission Factors throughout a broad radioisotope energy range were measured. According to findings, holmium (Ho) incorporation into the glass structure resulted in a net increase of 0.3406 g/cm3, whereas cerium (Ce) addition resulted in a net increase of 0.2047 g/cm3. The 40% WO3 reinforced S7 sample was found to have the greatest LAC value, even though seven glass samples exhibited identical behavior. The S2 sample had the lowest HVL values among the glass groups evaluated in this work, computed in the energy range of 0.015–15 MeV. The lowest EBF and EABF values were reported for 40% WO3 reinforced S7 sample with the highest LAC and density values. According to the findings of this research, WO3 will likely make a significant contribution to the gamma ray absorption properties of antimony glasses, which are employed for optical and structural modification. Therefore, it can be concluded that WO3 may be treated monotonically and can be employed successfully in circumstances where gamma-ray absorption characteristics, optical properties, and structural qualities need to be enhanced. © 2023 The Authors