The additive technology to obtain a three-dimensional model of the 81Cu-19Ni alloy

Abstract

This paper is devoted to the selective laser smelting (SLS) method description for the article made of powder of a Cu81-Ni19 copper-nickel alloy and the study of the structure and characteristics of the three-dimensional article made using additive technology. To make a 3D model the copper-nickel alloy powder was produced in our laboratory. The chemical composition, microstructure, density, surface roughness and microhardness of an article made of powders of a Cu81-Ni19 copper-nickel alloy are considered. A comparative analysis of the structure, physical and mechanical properties of a sample obtained by the SLS method and the annealed rolled plate was carried out. The article microstructure is characterized by the absence of a typical signs of a crystalline structure and contains elements of a quasi-amorphous state. At the same time, the obtained material differs from the standard monolith billet with a lower surface roughness and a higher hardness values while maintaining almost the same density indices. © Published under licence by IOP Publishing Ltd.