Название: | The Positron and Mechanical Parameters of a Cold-Worked Aluminum Alloy (3004) Using PALT, PADBT and HV |
Авторы: | Mostafa, A. Mostafa, M. Y. A. Abdel-Rahman, M. Abdel-Rahman, M. A. Badawi, E. A. Lin, Y. C. |
Дата публикации: | 2021 |
Издатель: | De Gruyter Open Ltd Walter de Gruyter GmbH |
Библиографическое описание: | The Positron and Mechanical Parameters of a Cold-Worked Aluminum Alloy (3004) Using PALT, PADBT and HV / A. Mostafa, M. Y. A. Mostafa, M. Abdel-Rahman et al. // Journal of the Mechanical Behavior of Materials. — 2021. — Vol. 30. — Iss. 1. — P. 292-303. |
Аннотация: | In the present work, the influence of plastic deformation on the properties of a 3004 Al-alloy was studied with different techniques. Crystallite size, dislocation density, defect density, micro-strain, and stored dislocation energy are presented and compared for different three techniques. Methodology: Many techniques for detecting defects have been developed, such as the positron annihilation lifetime technique (PALT), the positron annihilation Doppler broadening technique (PADBT), and the Vickers hardness test (HV). Implications: The positron mean lifetime value of a non-deformed sample is 173±4.8 ps, which increases until the thickness reduction reaches a 10% deformation then saturated at saturation trapping of the positron in defect states with a mean of 221±5 ps. At an S-parameter of 0.3709±0.0031, a W-parameter of 0.5885±0.0057 was obtained at zero deformation: this decreases until saturation at 10% deformation. Findings: A good correlation between the three techniques is observed for mean crystallite size. A good correlation was also noted between PALT and PADBT from 0 to 10% thickness reduction. HV has good correlations with PALT and PADBT from 0 to 6% thickness reduction: then a clear difference was found from 6 to 15% thickness reduction. Originality: such results confirm the fact that the used technique can effects on the obtained results in some limitations. © 2021 Ahmed Mostafa et al., published by De Gruyter. |
Ключевые слова: | 3004 AL-ALLOY PLASTIC DEFORMATION POSITRON ANNIHILATION TECHNIQUES |
URI: | http://elar.urfu.ru/handle/10995/112086 |
Условия доступа: | info:eu-repo/semantics/openAccess |
Идентификатор SCOPUS: | 85126016426 |
Идентификатор WOS: | 000757961000001 |
Идентификатор PURE: | 29729113 |
ISSN: | 0334-8938 |
DOI: | 10.1515/jmbm-2021-0032 |
Располагается в коллекциях: | Научные публикации ученых УрФУ, проиндексированные в SCOPUS и WoS CC |
Файлы этого ресурса:
Файл | Описание | Размер | Формат | |
---|---|---|---|---|
2-s2.0-85126016426.pdf | 2,75 MB | Adobe PDF | Просмотреть/Открыть |
Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.