Наноструктурные алюмоматричные композиционные материалы с высокой удельной прочностью

Abstract

In this work aluminum-magnesium alloy was nanostructured through mechanical activation technique and modified with fullerenes C60. Excellent mechanical properties were obtained, such as bending strength up to 1100 MPa, microhardness up to 3300 MPa. The effect of additional magnesium doping and C60 fullerene modification on the structural-phase composition and the physical-mechanical properties of the resulting composites was studied.