Structural Investigations of Li1.5Al0.5Ge1.5(PO4)3 glass-ceramics by Solid State NMR

Abstract

NASICON-type conductors based on LiGe2(PO4)3 are very promising lithium-conducting electrolytes for all-solid-state lithium-ion and lithium batteries. Al-doped LiGe2(PO4)3 solid electrolytes possessed higher conductivity (∼10-4 S/cm at room temperature) and stability versus metallic Li. In this paper, we present the structure study of Li1.5Al0.5Ge1.5(PO4)3 compound. Fast lithium-ion conductor Li1.5Al0.5Ge1.5(PO4)3 solid electrolyte have been obtained through glass crystallization at 820 °C during 8 h. Structural positions occupied by atoms have been examined by solid state nuclear magnetic resonance experiments. 6Li, 7Li, 27Al 31P NMR measurements have been performed at room temperature. © Published under licence by IOP Publishing Ltd.