Texture and structure formation of low-carbon low-alloy pipe steel after TMCP and heat treatment

Abstract

The structure and texture of low-carbon low-alloy pipe steel after Thermo-Mechanical Controlled Processing (TMCP) and subsequent isothermal quenching were studied by the method of Electron Backscatter Diffraction (EBSD) analysis. The texture, obtained after TMCP, was formed mainly by two strong scattered orientations from {112}<110> and two weaker scattered orientations from {110}<223> and one weak orientation (001)[110]. Complex multicomponent textures were observed after heat treatment. The regions with "ferrite" and martensitic structures were identified and analyzed using Oxford Instruments HKL software. Orientations, constituting textures for both selected areas types, are associated with the basic orientations of the initial deformed austenite grains, formed during the hot deformation by orientation relationships (OR), transitory between Kurdjumov-Sachs OR and Nishiyami-Wasserman OR. © 2019 IOP Publishing Ltd. All rights reserved.