Люминесценция кристаллов Li6Y(BO3)3 с примесью ионов празеодима при различных типах возбуждения

Abstract

This paper reports the spectroscopic properties of praseodymium-doped borates, Li6Y(BO3)3:Pr3+(1%). Emission upon X-ray and cathode beam excitation as well as photoluminescence excitation spectra in region of 3.5 – 6.0 eV were studied. For this Pr3+-doped triple borates, the 4f15d – 4f2 radiation transitions with nanosecond decay kinetics (τ ≈ 16 ns) were detected. Besides both the 4f2 – 4f2 transitions and defect-related luminescence in visible and near IR regions were analyzed. Thermoluminescence glow was measured and parameters of charge carriers traps were determined.

В работе исследованы спектроскопические свойства легированных ионами празеодима соединений Li6Y(BO3)3:Pr3+ (1%). Изучено излучение при рентгеновском и импульсном катодном возбуждении, возбуждение фотолюминесценции в области 3,5 – 6,0 эВ. Для исследуемого материала были обнаружены быстрые 4f15d – 4f2 излучательные переходы с наносекундной кинетикой (τ ≈ 16 нс). Проведен анализ 4f2 – 4f2 переходов и люминесценции дефектов в видимой и ближней ИК областях. Проведены измерения кривой термовысвечивания, рассчитаны параметры ловушек носителей заряда.