Structure and mechanical properties of corrosion-resistant high-nitrogen 04Kh22AG15N8M2F and 05Kh19AG10N7MFB steels after hot deformation

Abstract

The structure and mechanical properties of corrosion-resistant high-nitrogen austenitic 04Kh22AG15N8M2F and 05Kh19AG10N7MFB steels are studied after hot rolling at 950 and 1100°C. The following specific features of the structure of hot-rolled 04Kh22AG15N8M2F steel are revealed: the presence of coarse grain-boundary precipitates of the molybdenum-rich σ phase and its nonuniform distribution over the volume of austenite grains. The 05Kh19AG10N7MFB steel hot rolled at 950°C contains ultrafine carbonitrides particles and has the best combination of a high strength and a sufficient elasticity and impact toughness. The structures of the hot-rolled steels have no ferrite, martensite, and traces of recrystallized austenite grains. © 2012 Pleiades Publishing, Ltd.