Результаты исследования вихревых зон, полученных при сварке взрывом ниобия и нержавеющей стали

Abstract

In this article described results about researching of the structure and microhardness compound niobium foil and stainless steel plate which produced by explosion welding. It is shown that the boundary between the welded materials has a undulatory character. The mixing zones formed in some parts of the boundary of two materials. Microhardness exceeds of these areas greatly than microhardness starting materials. The mixing zones have amorphous structure. This structure determined by means of transmission electron microscopy. This fact is evidence that process of explosion welding had the high cooling rates that typically for explosion welding.

В работе представлены результаты исследования структуры и микротвёрдости соединения фольги ниобия и пластины нержавеющей стали, полученные методом сварки взрывом. Показано, что граница между свариваемыми материалами имеет волнообразный характер. В отдельных участках границы образуются зоны перемешивания двух материалов. Микротвёрдость этих участков существенно превышает микротвёрдость исходных материалов. Методом просвечивающей электронной микроскопии установлено, что зоны перемешивания склонны к формированию аморфной структуры. Этот факт свидетельствует о высоких скоростях охлаждения, имеющих место при сварке взрывом.