Влияние режимов диффузионной сварки и термообработки на структуру и механические свойства пористых заготовок из титанового волокна

Abstract

The effect of diffusion welding modes on structure and properties of PM from titanium fibers was investigated. It was shown that the perspective area in PM production for medical application could be the use of titanium fibers obtained by high-speed melt solidification and joined by diffusion welding in workpieces or articles. It was stated that the change in type of fibers structure and their junctions had a substantial influence on mechanical characteristics of PM workpieces. We also observed PM strength increase and plasticity decrease at the growth of diffusion welding temperature for sheet workpieces as well as for cylindrical ones.

Проведено исследование влияния режимов диффузионной сварки на структуру и свойства ПМ из волокон титана. Показано, что перспективным направлением получения ПМ для медицинского применения может быть использование волокон титана, полученных высокоскоростным затвердеванием расплава, соединенных в заготовки или изделия методом диффузионной сварки. Установлено, что изменение характера структуры волокон и их контакта оказывает существенное влияние на механические характеристики заготовок ПМ. Отмечено, что с повышением температуры диффузионной сварки как для листовых, так и для цилиндрических заготовок наблюдается увеличение прочности и снижение пластичности ПМ.