Название: | Effect of additions of zinc stearate on the properties of sintered Nd-Fe-B magnets |
Авторы: | Popov, A. G. Gerasimov, E. G. Terent'ev, P. B. Gaviko, V. S. Shunyaev, K. Y. Mikhailova, T. L. Vas'kovskii, V. O. Kulesh, N. A. |
Дата публикации: | 2013 |
Библиографическое описание: | Effect of additions of zinc stearate on the properties of sintered Nd-Fe-B magnets / A. G. Popov, E. G. Gerasimov, P. B. Terent'ev [et al.] // Physics of Metals and Metallography. — 2013. — Vol. 114. — № 4. — P. 285-294. |
Аннотация: | Zinc stearate additions have been used to increase the remanence of sintered Nd-Fe-B magnets produced by the powder metallurgy without powder pressing. Zinc stearate acts as an internal lubricant, i.e., it decreases the friction forces between the particles and favors an increase in the degree of texture of the powders, which is induced by the magnetic field. It is shown that the density and the magnetic hysteresis characteristics of sintered magnets produced using additions of 0.15 wt % zinc stearate exceeds the corresponding values obtained for magnets produced without this addition at a filling density of powders in containers of more than 2.9 and 3.0 g/cm3 in dry and wet states, respectively. Using additions of zinc stearate in the amount of 0.15% with respect to the weight of the powder, magnets with a density of 7.55 g/cm3, B r = 14.02 kG, H c = 7.91 kOe, and (BH)max = 46.1 MG Oe have been produced. © 2013 Pleiades Publishing, Ltd. |
Ключевые слова: | INTERNAL LUBRICANTS ND-FE-B ALLOYS POWDER METALLURGY METHOD PRESSLESS PROCESS (PLP) SINTERED MAGNETS ZINC STEARATE EFFECT OF ADDITION HYSTERESIS CHARACTERISTICS ND-FE-B ALLOY POWDER PRESSING PRESSLESS PROCESS (PLP) SINTERED MAGNETS SINTERED NDFEB MAGNET ZINC STEARATE FILLING FRICTION LUBRICANTS MAGNETS NEODYMIUM NEODYMIUM ALLOYS POWDER METALLURGY POWDERS SINTERING ZINC |
URI: | http://elar.urfu.ru/handle/10995/27062 |
Идентификатор SCOPUS: | 84877826185 |
Идентификатор WOS: | 000318179800002 |
Идентификатор PURE: | 916551 |
ISSN: | 0031-918X 1555-6190 |
DOI: | 10.1134/S0031918X13040066 |
Располагается в коллекциях: | Научные публикации ученых УрФУ, проиндексированные в SCOPUS и WoS CC |
Файлы этого ресурса:
Файл | Описание | Размер | Формат | |
---|---|---|---|---|
scopus-2013-0240.pdf | 1,21 MB | Adobe PDF | Просмотреть/Открыть |
Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.