Magnetic properties and giant magnetoimpedance of surface modified Co-based amorphous ribbons with carbon covering

Abstract

Fe3Co66Cr3Si16B12 and Fe6Co60Ni10Si14B10 amorphous ribbons were surface modified in toluene at room temperature. Such a treatment resulted in deposition of thin carbon-based layer. As a result of the carbon covering deposition the stress distribution in the near-surface layers was changed due to partial compensation of the initial quenching stresses. Comparative analysis of magnetic and magnetoimpedance properties of as-quenched and surface modified ribbons confirms changes in effective magnetic anisotropy as a result of surface treatment. An increase of the corrosion resistance of the ribbons with carbon covering can be useful for the development amorphous ribbon based magnetic biosensor. © 2018 The Authors, published by EDP Sciences.