Соединения Sm-Fe-Ti как новый материал для постоянных магнитов

Abstract

Synthesis and heat treatment by various methods of compounds (Sm,M)(Fe,Co)Ti, where M = Zr, Hf, with the ThMn12 structure (1-12) were carried out in the work. The results of their thermomagnetic phase analysis, metallographic analysis of the structure, and measurement of the specific saturation magnetization (σs) are presented. The effect of the annealing temperature and the cooling rate on the formation of phase 1-12, and its magnetic properties was established. The obtained compound (Sm0.8Zr0.2)(Fe-Co)11.4Ti0.6 having σs = 112.6 Gs*cm3/g (H = 12 kOe) and Curie temperature (Tc) = 600 °C, is a potential candidate for the creation permanent magnets (1-12).

В работе проведен синтез и термообработка различными методами соединений (Sm,M)(Fe,Co)Ti, где М = Zr, Hf, со структурой ThMn12 (1-12). Представлены результаты их термомагнитного фазового анализа, металлографического анализа структуры и измерения удельной намагниченности насыщения (σs). Установлено влияние температуры отжигов и скорости остывания на формирование фазы 1-12, и её магнитные свойства. Полученное соединение (Sm0.8Zr0.2)(Fe-Co)11.4Ti0.6, обладающее σs = 112.6 Гс*см3/г (H = 12 кЭ) и температурой Кюри (Тс) = 600 ºС, является потенциальным кандидатом для создания постоянных магнитов (1-12).