Формирование структуры двухфазной высокоазотистой Cr–Mn–Mo-стали при тепловой обработке

Abstract

We studied the structure of nickel-free Cr–Mn–Mo steel with a high nitrogen content (0,34 %), formed as a result of heat treatment according to different quenching and aging schemes. The metallographic method, X-ray phase analysis and hardness measurement were used. During heat treatment, the austenite and ferrite of the studied steel decomposed with the formation of nitrides and the intermetallic s-phase and experienced polymorphic transformations. Separation of ferrite was also observed with the formation of a chromium-enriched phase. A duplex structure (with a content of each phase of about 47 %) was obtained after quenching from 1150 °C and aging at 700 °C.

Исследовали структуру безникелевой Cr–Mn–Mo-стали с высоким содержанием азота (0,34 %), образующуюся в результате термической обработки по разным схемам закалки и старения. Использовали металлографический метод, рентгеноструктурный фазовый анализ и измерение твердости. В процессе термообработки аустенит и феррит распадались с образованием нитридов и интерметаллидной s-фазы и испытывали полиморфные превращения. Наблюдалось также расслоение феррита с образованием обогащенной хромом фазы. Дуплексная структура (с содержанием каждой фазы около 47 %) была получена после закалки от 1150 °C и старения при 700 °C.