Влияние обработки в высокоэнергетической планетарной шаровой мельнице на морфологию и структуру частиц порошка сплава Fe66Cr10Nb5B19

Abstract

In the present work, the morphology and phase changes occurring upon treatment of a Fe66Cr10Nb5B19 powder in a high-energy planetary ball mill were studied. The powder alloy was obtained by gas atomization and consisted of crystalline phases. It was found that mechanical treatment resulted in amorphization of the alloy. An increase in the content of the amorIn the present work, the morphology and phase changes occurring upon treatment of a Fe66Cr10Nb5B19 powder in a high-energy planetary ball mill were studied. The powder alloy was obtained by gas atomization and consisted of crystalline phases. It was found that mechanical treatment resulted in amorphization of the alloy. An increase in the content of the amor-phous phase in the alloy with an increase in the treatment time from 2 min to 10 min was caused by accumulation of non-equilibrium defects in the structure of the alloy.

В работе представлены результаты исследования влияния обработки в высокоэнергетической планетарной шаровой мельнице на морфологию частиц и фазовый состав порошка сплава Fe66Cr10Nb5B19. Исходный порошок сплава получен методом газового распыления и имеет кристаллическую структуру. Установлено, что механическая обработка порошка сплава приводит к его аморфизации. Увеличение содержания аморфной фазы с увеличением времени механической обработки от 2 до 10 мин связано с накоплением неравновесных дефектов в структуре сплава.