Abstract

Ag2S nanoparticles were synthesized by the method of chemical condensation in an aqueous solution. To assess the effect of the stabilizing agent, diluted and undiluted in alcohol MPS and various molar ratios of AgNO3 to Na2S were used. The synthesized colloidal Ag2S solutions were used to make films in several ways. The colloidal solutions and films were studied by dynamic light scattering, optical microscopy, and atomic force microscopy. The stability area of the colloidal Ag2S solution was determined. It was found that the particle size and size distribution in the films depends on the concentration of the starting reagents. The method of creating a thin film with the smallest size of Ag2S nanoparticles was developed. The self-organization of nanoparticles was discovered during the formation of a multilayer film with a diameter of particles from 0.5 to 15 .m.

Методом химической конденсации синтезированы наночастицы Ag2S в водном растворе. Для оценки влияния стабилизирующего агента использованы разбавленный и неразбавленный в спирте МПС, и различные молярные соотношения AgNO3 к Na2S. Из синтезированных коллоидных растворов Ag2S несколькими способами изготовлены пленки. Коллоидные растворы и пленки изучались методами ДРС, оптической микроскопии и АСМ. Определена область стабильности коллоидного раствора сульфида серебра. Установлено, что размер частиц и распределение по размерам в пленках зависит от концентрации исходных реагентов. Предложен вариант создания тонких пленок с большим количеством агломератов, меньших по размеру, на поверхности подложки. Обнаружена самоорганизация наночастиц при формировании многослойной пленки диаметром от 0.5 до 15 мкм.