Исследование электрических свойств диселенида гафния, интеркалированного медью и серебром, методом импедансной спектроскопии

Abstract

The features of charge transfer in intercalated CuxHfSe2 and AgуHfSe2samples were first studied on alternating current using the technique of impedance spectroscopy. The acceleration of relaxation processes in an alternating field with increasing silver content in the samples was revealed. Complex conductivity (Yac) experiences a frequency dispersion, which is described by the power law Yac ~ .n, which is characteristic of the hopping conduction mechanism. Shorter relaxation times were obtained for AgyHfSe2 compounds compared with those observed in hafnium diselenide samples intercalated by copper atoms, which indicates a higher mobility of charge carriers in compounds intercalated with silver.

Особенности переноса заряда в интеркалированных образцах CuxHfSe2 и AgуHfSe2 впервые исследованы на переменном токе с использованием методики импедансной спектроскопии. Выявлено ускорение релаксационных процессов в переменном поле при возрастании содержания серебра в образцах. Комплексная проводимость (Yac) испытывает частотную дисперсию, которая описывается степенным законом Yac ~ .n, что характерно для прыжкового механизма проводимости. Для соединений AgуHfSe2 получены меньшие времена релаксации по сравнению с наблюдаемыми в образцах диселенида гафния, интеркалированного атомами меди, что свидетельствует о большей подвижности носителей заряда в соединениях, интеркалированных серебром.