Abstract

FIELD: binding agents. SUBSTANCE: invention relates to compositions comprising water-resistant gypsum binding agents containing active mineral additives including calcium, aluminum oxides and silica. The gypsum binding agent based on calcium sulfate semihydrate with mineral additive as high-calcium ash and organic additive comprises granulated high-calcium fly ash as a mineral additive obtained after combustion of solid fuel and crushed to residue on sieve 008 in the amount 5%, not above, and plasticizing agent as an organic additive, and components are taken in the following ratio, wt.-%: calcium sulfate semihydrate, 73.9-90; plasticizing agent, 1.1-2.0, and indicated fly ash, the balance. Invention provides enhancing strength and water resistance of a binding agent, decreasing cost of composition and utilizing a definite part of solid exhaust in thermal power field. EFFECT: improved and valuable properties of binding agent.

Изобретение относится к составам водостойких гипсовых вяжущих, содержащих активные минеральные добавки, включающие оксиды кальция, алюминия, кремнезем. Технический результат - повышение прочности и водостойкости вяжущего, а также удешевление композиции и утилизация определенной части твердых выбросов теплоэнергетики. В гипсовом вяжущем на основе полугидрата сульфата кальция с минеральной добавкой в виде высококальциевой золы и органической добавкой, в качестве минеральной добавки используют гранулированную высококальциевую золу-унос от сжигания твердого топлива, размолотую до остатка на сите 008 не более 5%, а в качестве органической - пластификатор, при следующем соотношении компонентов, мас.%: полугидрат сульфата кальция - 73,9-90, пластификатор - 1,1-2,0, указанная зола-унос высококальциевая - остальное.