Title: Способ изготовления спеченных многослойных изделий
Other Titles: METHOD FOR MAKING SINTERED STRATIFORM ARTICLES
Patent Number: 2014956
Authors: Беляев, А. А.
Гуцо, Д. Э.
Киселев, В. М.
Тарасов, К. А.
Issue Date: 1994-06-30
Abstract: FIELD: powder metallurgy. SUBSTANCE: method involves charging, pressing and sintering layers of powder. Said layers are pressed at a pressure of 200-10 MPa, reducing said pressure in each subsequent layer at least by 10 MPa. Layers are sintered in vacuum, increasing sintering temperature of each subsequent layer by 20-30 K. After sintering the last layer, the article is heated in vacuum to a temperature 5-15 K higher than the destruction temperature of oxide layers on surface of powder particles in the course of 10-30 s. EFFECT: higher efficiency.
Изобретение относится к порошковой металлургии. Последовательно засыпают, прессуют и спекают слои порошка, прессование слоев осуществляют при давлении 200 - 10 МПа с уменьшением давления прессования каждого последующего слоя не менее чем на 10 МПа, спекание слоев осуществляют в вакууме при увеличении температуры спекания каждого последующего слоя на 20 - 40 К. После спекания последнего слоя изделие нагревают в вакууме до температуры на 5 - 15 К выше температуры разрушения оксидных слоев на поверхности частиц порошка в течение 10 - 30 с.
Keywords: PATENT
INVENTION
ПАТЕНТ
ИЗОБРЕТЕНИЕ
URI: http://hdl.handle.net/10995/83834
RSCI ID: 41060809
Patent Type: Патент на изобретение
Patent Owner: Уральский государственный университет им.А.М.Горького
Appears in Collections:Патенты и изобретения

Files in This Item:
File Description SizeFormat 
2014956.pdf221,56 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.