Исследование эволюции структуры и механических свойств бериллиевых фольг при холодной прокатке и термической обработке с помощью методов EBSD-анализа

Abstract

Investigations of beryllium structure evolution during cold rolling and high-vacuum heat treatment by different regimes were performed in this work using EBSD analysis. It’s established that combination of large total strain at cold rolling and short-term high-vacuum annealings is necessary to beryllium fine-grained microstructure formation in thin foils and the required complex of mechanical properties obtaining. The proportion of crystallites with favorable {0001} <uvw> type texture grows in foils as total strain at cold rolling increases. This promotes to plastic properties increase due to additional non–basic slip systems activation during deformation.

В работе при помощи методов EBSD анализа выполнены исследования эволюции структуры бериллиевых фольг при холодной прокатке и высоковакуумной термической обработке по различным режимам. Установлено, что для формирования мелкозернистой структуры бериллия в тонких фольгах и получения высокого уровня механических свойств необходимо использование больших суммарных деформаций при холодной прокатке в сочетании с кратковременными высоковакуумными отжигами. Увеличение суммарной степени деформации при холодной прокатке приводит к увеличению доли кристаллитов с благоприятной компонентой текстуры в фольге типа {0001}<uvw>, которая способствует повышению пластических свойств за счет активации дополнительных небазисных систем скольжения при деформации.