ПЭМ–структура электровзрывного покрытия Sno2–Ag, сформированного на медных контактах переключателей мощных электрических сетей

Abstract

The studies of the phase and elemental composition of the surface layer copper electric contact of KPV‑604 contactor subjected to electroexplosion spraying of the composite SnO2–Ag-system coating were done by the method of transmission electron microscopy. The scale of the elemental structure of the coating’s surface varies within a very wide interval after the electroexplosion spraying — from hundreds of micrometers to tens of hundreds of nanometers. According to the morphological feature two layers may be distinguished in the coating’s volume: the coating proper and the thermal effect layer smoothly transferring to the bulk of the sample. The nanocrystalline structure was detected.

Методом просвечивающей электронной микроскопии выполнены исследования фазового и элементного состава поверхностного слоя медного электрического контакта контактора КПВ‑604, подвергнутого электровзрывному напылению композиционного покрытия системы SnO2–Ag. Масштаб элементов структуры поверхности покрытия после электровзрывного напыления изменяется в очень широком интервале — от сотен микрометров до десятков — сотен нанометров. По морфологическому признаку в объеме покрытия можно выделить два слоя: собственно покрытие и слой термического влияния, плавно переходящий в основной объем образца. Выявлено образование многоэлементного многофазного покрытия, имеющего нано-кристаллическую структуру.