Структура и свойства штамповых сталей после модификации электровзрывным методом

Abstract

The modification of the surface layer of 5CrNiMo and Cr12MoV steels was done by the electroexplosion method. The formation of hardening structure presented by the packet and lamellar (twinned) martensite is revealed in the modified layer of 5CrNiMo steel. It is stated that the hardening phase of the modified layer of Cr12MoV steel is the nanodimentional particles of iron and titanium carbides. The electroexplosion modification of Cr12MoV steel is accompanied by the structure formation of the lamellar morphology pearlite containing the round inclusions of the second phase of submicron sizes. It is stated that the electroexplosion method modification of 5CrNiMo and Cr12MoV steels contributes to the increase in microhardness and wear resistance of the material and it is most pronounced in the case of Cr12MoV steel.

Электровзрывным методом осуществлено модифицирование поверхностного слоя стали марки 5ХНМ и Х12МФ. Выявлено формирование закалочной структуры, представленной пакетным и пластинчатым (двойниковым) мартенситом. Установлено, что упрочняющей фазой модифицированного слоя стали 5ХНМ являются наноразмерные частицы карбидов железа и титана. Электровзрывное модифицирование стали марки Х12МФ сопровождается формированием структуры перлита пластинчатой морфологии, содержащей округлые включения второй фазы субмикронных размеров. Установлено, что модифицирование электровзрывным методом стали марки 5ХНМ и Х12МФ способствует повышению микротвердости и износостойкости материала, что особенно ярко выражено в стали марки Х12МФ.