Способ получения высокочистых веществ

Abstract

FIELD: synthesis of wide range of high-purity materials applicable in laser and infrared engineering, and also in fiber optics and special engineering. SUBSTANCE: method includes dissolving of initial substances in solvent, supersaturation of solution and crystallization. Solubility of initial substances amounts up to 1.5-3.0 g/cu.dm at temperatures of 80-100 C with supersaturation degree of 0.5-2.0 g/cu.dm and supercooling temperature of 10-30 C. Ratio of constants of crystallization rates of components of crystallized compounds is not above 15, and induction periods do not exceed 1 min. For one cycle of thermozone crystallization in form of synthesis, purification from impurities is attained up to three orders of magnitude and more. EFFECT: developed base ecologically clean, closed, highly economically efficient and practically wasteless method with combined processes of synthesis of multicomponent compounds and their purification.

Используется для синтеза широкого класса высокочастотных материалов, применяемых в лазерной и инфракрасной технике, а также в волоконной оптике и спецтехнике. Способ включает растворение исходного вещества в растворителе, создание пересыщения раствора и кристаллизацию. Растворимость исходных веществ составляет 1,5 - 3,0 г/дм3 при температурах 80 - 100oC, степень пересыщения 0,5 - 2,0 г/дм3 и переохлаждения 10 - 30oC. Отношение констант скоростей кристаллизации компонентов, входящих в состав кристаллизуемых соединений, не выше 15, а периоды индукции не более 1 мин. Разработан базовый экологически чистый, замкнутый, высокоэкономичный и практически безотходный способ, в котором процессы синтеза многокомпонентных соединений и их очистка совмещены. За один цикл термозонной кристаллизацией - синтезом (ТЗКС) очистка от примесей достигается до трех порядков и более.