FIELD: metallurgy. SUBSTANCE: invention relates to ferrous metallurgy, particularly it relates to electric furnace steelmaking. Method includes charging of metal stock, consisting of metallurgical scrap, cast iron, metallised pellets or briquettes, converter vanadium slag, metal stock melting. In metal stock it is used 30-50% of metallized pellets or briquettes, non containing titanium and vanadium oxide, and vanadium-bearing cast iron with vanadium content 0.5-0.6%. Mass portion of converter vanadium slag of metallised pellets mass is 2-10%, portion of vanadium cast iron of metal stock mass is 10-15%. Before feeding of pellets or briquettes into electroarc furnace is implemented its heating up to the temperature 300-500°C and post reduction by effluent gases of arc furnace. EFFECT: alloying of steel by vanadium during reduction in steel impurities of nonferrous metal. 3 cl, 1 dwg.

Изобретение относится к черной металлургии, в частности к электросталеплавильному производству. Способ включает загрузку металлошихты, состоящей из металлургического лома, чугуна, металлизированных окатышей или брикетов, конверторного ванадиевого шлака, плавление металлошихты. В металлошихте применяют 30-50% металлизированных окатышей или брикетов, не содержащих оксида титана и ванадия, и ванадийсодержащий чугун с содержанием ванадия 0,5-0,6%. Доля массы конверторного ванадиевого шлака от массы металлизированных окатышей составляет 2-10%, доля ванадиевого чугуна от массы металлошихты составляет 10-15%. Перед подачей окатышей или брикетов в электродуговую печь осуществляют их подогрев до температуры 300-500°С и довосстановление отходящими газами дуговой печи. Использование изобретения позволяет обеспечить легирование стали ванадием при снижении в стали примесей цветных металлов. 2 з.п. ф-лы, 1 ил.