Гранулометрический состав продуктов разрушения железорудных агломератов из железистых кварцитов при восстановлении

Abstract

The regularities of formation of the granulometric composition of decay products of iron ore sinter in test ISO 13930. It is found that the growth of the tumble index + 5mm is accompanied by an increase in the size of the sinter fracture products during recovery; with an increase in the basicity of the agglomerate, both "cold" and "hot" strength increases; the yield of the class –0,5 mm during recovery (LTD–0,5) decreases as the abrasion of the agglomerate increases. It is determined that the formation of dust of class –0,5 mm from the sinter is caused only by mechanical abrasion during its transportation and passage through the shaft of the blast furnace, with little impact of internal stresses.

Исследованы закономерности формирования гранулометрического состава продуктов разрушения железорудного агломерата при испытании по ISO 13930. Установлено, что рост барабанной пробы +5 мм сопровождается повышением крупности продуктов разрушения спека при восстановлении; при повышении основности агломерата растет как «холодная», так и «горячая» прочности; выход класса –0,5 мм при восстановлении (LTD–0,5) снижается по мере роста истираемости агломерата. Определено, что формирование пыли класса –0,5 мм из агломерата обусловлено только механическим истиранием при его транспортировке и прохождении через шахту доменной печи, при незначительном влиянии внутренних напряжений.