Автоклавное выщелачивание концентратов уральских горно-обогатительных фабрик

Abstract

An alternative approach to the processing of copper concentrates of the Ural enrichment plants is considered. Experiments were carried out on pressure leaching of the concentrate with the following composition, %: 21.5 Cu, 0.1 Zn, 0.05 Pb, 0.04 Ni, 26.59 S, 24.52 Fe, 16.28 SiO2. Two variants of the process directing are considered - high-temperature and low-temperature autoclave oxidative leaching, for which optimal process parameters are proposed: t = 190–210 °C, PO2 = 0.4–0.6 MPa, СН2SO4 = 0–15 g/L and t = 105–108 °C, PO2 = 1.3–1.5 MPa, CH2SO4 = 75–90 g/L, respectively. The chemical composition of leach products is given and ways of their further processing are suggested.

В работе рассмотрен альтернативный подход к переработке медных концентратов Уральских горно-обогатительных фабрик. Проведены эксперименты по автоклавному выщелачиванию концентрата следующего состава, %: 21,5 Cu, 0,1 Zn, 0,05 Pb, 0,04 Ni, 26,59 S, 24,52 Fe, 16,28 SiO2. Рассмотрены два варианта ведения процесса - высокотемпературное и низкотемпературное автоклавное окислительное выщелачивание, для которых предложены оптимальные параметры ведения процесса: t = 190–210 °C, PO2 = 0,4–0,6 МПа, СH2SO4= 0–15 г/дм3 и t = 105–108 °C, PO2 = 1,3–1,5 МПа, СH2SO4= 75–90 г/дм3 соответственно. Приведен химический состав продуктов выщелачивания и предложены пути их дальнейшей переработки.