Электронно-микроскопические исследования структурно-фазового состояния и радиационного распухания аустенитных сталей после имитационных испытаний с использованием ускорителей

Abstract

Presently, the new austenitic materials for reactor internals worked out. To estimate their irradiation durability, instead of the traditional technology of preparation of irradiation coupon, it was applied imitation of irradiation damage by the irradiation in ion accelerators. Microstructural changes were examined using of method of precision preparation by focused ion beam in a scanning double-beam electron-ion microscope. Then the prepared samples was study in a transmission electron microscope. There has been developed and tested method of determining the bulk density of vacancy voids and their size distribution. Elemental and phase analysis of secondary phases has been performed . Obtained profiles of injected ions.

В настоящее время разработаны новые аустенитные материалы для ВКУ. Для оценки их радиационной стойкости, вместо традиционной технологии пробоподготовки образцов-свидетелей, была применена имитация радиационного повреждения при облучении ионами в ускорителях. Микроструктурные изменения были исследованы с помощью методики прецизионного препарирования сфокусированным ионным пучком на растровом двулучевом электронно-ионном микроскопе, с последующим изучением приготовленных образцов на просвечивающем микроскопе. Разработана и опробована методика определения объемной плотности вакансионных пор и их распределения по размерам. Проведен элементный и фазовый анализ вторичных фаз. Получены профили распределения инжектированных ионов.