Текстура горячекатаного алюминиевого сплава

Abstract

The method of orientation microscopy investigated the texture of hot rolled aluminum alloys 6061 and 7050 along the entire thickness of the substrate. It is shown that the deformation texture of both surface and central layers of the strip, consists of a set of discrete, stable orientations. The texture of the surface layer, is deployed at 90° around the transverse direction, the texture of the central layer. The recrystallization texture is mainly composed of the same orientations as the texture deformation. The formation of such multi-component textures, can be explained based on the hypothesis that moving in recrystallization processes are a special border.

Методом ориентационной микроскопии (EBSD) исследована текстура горячекатаных алюминиевых сплавов 6061 и 7050 по всей толщине подката. Показано, что текстура деформации как поверхностного, так и центрального слоев полосы, состоит из набора дискретных, стабильных ориентировок. Текстура поверхностного слоя, является развернутой на 90° вокруг поперечного направления, текстурой центрального слоя. Текстура рекристаллизации преимущественно состоит из тех же ориентировок, что и текстура деформации. Формирование подобного рода многокомпонентных текстур, может быть объяснено исходя из гипотезы, что подвижными в рекристаллизационных процессах являются специальные границы.