Способ изготовления литий-ионного источника тока с анодом на основе кремния

Abstract

FIELD: distributed power engineering. SUBSTANCE: invention relates to portable electric energy storage devices with improved energy characteristics. Method of making a lithium-ion current source with an anode based on silicon involves electrodeposition of a solid film of silicon from a molten electrolyte on a graphite current lead and use of obtained composition as anode with current lead in unit cell of lithium-ion current source, note here that electrodeposition of 1–8 mcm thick silicon film on graphite current lead is performed from molten chloride-fluoride electrolyte LiCl-KCl-CsCl-K₂SiF₆ at temperature not higher than 650 °C. EFFECT: reduction of costs for production of anode material of lithium-ion current source, expansion of range of permissible materials of current lead to anode, reduction of oxygen in composition of anode of lithium-ion current source and increase of its specific capacity. 1 cl, 2 dwg.

Изобретение относится к распределенной энергетике, в частности к портативным устройствам накопления электрической энергии с улучшенными энергетическими характеристиками. Способ изготовления литий-ионного источника тока с анодом на основе кремния включает электроосаждение сплошной пленки кремния из расплавленного электролита на графитовый токоподвод и использование полученной композиции в качестве анода с токоподводом в элементарной ячейке литий-ионного источника тока, при этом электроосаждение сплошной пленки кремния толщиной от 1 до 8 мкм на графитовый токоподвод осуществляют из хлоридно-фторидного расплавленного электролита LiCl-KCl-CsCl-K₂SiF₆ при температуре не выше 650°С. Технический результат заключается в снижении затрат на производство анодного материала литий-ионного источника тока, расширении диапазона допустимых материалов токоподвода к аноду, уменьшении кислорода в составе анода литий-ионного источника тока и повышении его удельной емкости. 2 ил.