|Title:||Phase Transitions in the Co–Al–Nb–Mo System|
|Citation:||Phase Transitions in the Co–Al–Nb–Mo System / D. Davydov, N. Kazantseva, N. Popov et al. // Metals. — 2021. — Vol. 11. — Iss. 12. — 1887.|
|Abstract:||Phase transitions in the Co-rich part of the Co–Al–Nb–Mo phase diagram are studied by energy dispersive spectroscopy (EDS), X-ray analysis, transmission electron microscopy (TEM), and differential scanning calorimetry (DSC) measurements. The obtained results were compared with the results for alloys of the binary Co–Al and ternary Co–Al–Nb, and Co–Al–Mo systems. Formation of the intermetallic phase with the L12 structure was found in a range of alloys with 10 at.% Al, 2–9 at.% Nb, and 3–7 at.% Mo. Intermetallic compound Co2Nb, Laves phase with the different chemical composition and crystal structure (C14 and C36) was detected in the Co–Al–Nb and Co–Al–Nb–Mo samples after vacuum solution treating at 1250◦C for 30 h. © 2021 by the authors. Licensee MDPI, Basel, Switzerland.|
HEAT RESISTANT SUPERALLOYS
|metadata.dc.description.sponsorship:||This work was founded by the Russian Foundation for Basic Research (RFBR), project No. 20-33-70221 and Russian State program of Institute of Metal Physics "Additivity" № 121102900049-1.|
|Appears in Collections:||Научные публикации, проиндексированные в SCOPUS и WoS CC|
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.