СОСТАВ И СПОСОБ СИНТЕЗА СЦИНТИЛЛЯЦИОННОЙ КЕРАМИКИ НА ОСНОВЕ НАНОПОРОШКА

Abstract

FIELD: chemistry. SUBSTANCE: group of inventions relates to the field of scintillation technology used to register ionizing radiation. Disclosed is the composition of scintillation ceramics based on yttrium alumina garnet doped with cerium ions (Ce3+:Y3Al5O12) made of a mixture of nanopowders of yttrium oxide doped with cerium ions (Ce:Y2O3), aluminum oxide (Al2O3), and yttrium oxide (Y2O3). Yttrium oxide is added to maintain stoichiometry, if necessary. The composition contains a sintering additive. Zirconium (Zr) is used as a sintering additive in the form of zirconium oxide ZrO2 with the content of 0.05-0.15 wt.%. EFFECT: increased speed of the ceramic scintillator without reducing the glow intensity. 2 cl, 2 dwg, 1 tbl.

Группа изобретений относится к области сцинтилляционной техники, применяемой для регистрации ионизирующих излучений. Состав сцинтилляционной керамики на основе алюмоиттриевого граната, активированного ионами церия (Ce³⁺:Y₃Al₅O₁₂), изготовленной из смеси нанопорошков оксида иттрия, допированного ионами церия (Ce:Y₂O₃), оксида алюминия (Al₂O₃) и оксида иттрия (Y₂O₃), при необходимости добавления последнего с целью сохранения стехиометрии, и содержащей спекающую добавку, при этом в качестве спекающей добавки содержит цирконий (Zr) в виде оксида циркония ZrO₂с содержанием 0,05-0,15 мас.%. Технический результат – повышение быстродействия керамического сцинтиллятора без снижения интенсивности свечения. 2 н.п. ф-лы, 1 табл., 2 ил.