Title: Preparation and analysis of Pr-Ga-Al alloys
Authors: Ismailov, M. Sh.
Melchakov, S. Yu.
Yamshchikov, L. F.
Volkovich, V. A.
Ovchinnikova, L. A.
Issue Date: 2019
Publisher: American Institute of Physics Inc.
Citation: Preparation and analysis of Pr-Ga-Al alloys / M. Sh. Ismailov, S. Yu. Melchakov, L. F. Yamshchikov, et al. — DOI 10.1063/1.5134175 // AIP Conference Proceedings. — 2019. — Vol. 2174. — 020024.
Abstract: Pr-Ga-Al alloys were prepared from individual praseodymium, gallium and aluminum purified from oxide films in an inert atmosphere of the glove box. The Ga-Al phase diagram was used to choose the eutectic composition (2.1 mol. % Al). The metals were mixed in a certain proportion in crucibles (BeO) and annealed at 832.4±1.7 °C and 366.2±6.3 °C for 19 hours and 53 hours, respectively. Three ingots were obtained with different praseodymium content. The alloys were investigated by X-ray phase analysis, scanning electron microscopy and electron backscatter diffraction technique. A general chemical analysis was also performed. Depending on praseodymium content the alloys consisted of PrGa6 intermetallic compound phase; a mixture of PrGa6 and ϵ-PrGa2 IMCs; and ϵ-PrGa2 phase. Ternary intermetallic compounds of praseodymium were not detected. A small addition of aluminum does not affect the phase characteristics of intermetallic compounds of praseodymium in alloys. © 2019 Author(s).
URI: http://hdl.handle.net/10995/101631
Access: info:eu-repo/semantics/openAccess
SCOPUS ID: 85076603125
PURE ID: 11751305
7bab01f1-2262-4146-bc2a-fbad7ee6d6ca
ISSN: 0094243X
ISBN: 9780735419216
DOI: 10.1063/1.5134175
Appears in Collections:Научные публикации, проиндексированные в SCOPUS и WoS CC

Files in This Item:
File Description SizeFormat 
2-s2.0-85076603125.pdf139,7 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.