Magnetic properties of Co-W thin films

Abstract

In this paper, the magnetic properties and structure of the Co-W films of different compositions prepared by magnetron sputtering on glass substrates without and with Ta or Ru buffer layers were investigated. The dependences of coercive force on the W content for the studied films were non-monotonic. The peak value of the coercive force of about 400 Oe was observed for the films on glass and Ta layers with W content of 8-9 at. %. The films deposited on Ru layers had a coercive force of 4 times less, and it was practically independent of the W content in a wide range from 6 to 20 at. %. © Published under licence by IOP Publishing Ltd.