Расширяющая добавка к цементу

Abstract

FIELD: chemistry. SUBSTANCE: invention refers to the composition of cement expansion agent and can be used in the industry of constructions materials and in petroleum industry for production of high-performance binders and grouting mortars. The cement expansion agent containing the dross of secondary aluminium reprocessing contains the said dross with following composition (wt %): Al₂O₃ 65-70, AlN₃ 10-15, Al 1-5, NaCl-KCl 10-23. The said dross is modified with organic acid includes particle size less than 100 mcm and taken in amount 0.1-1 wt % in relation to the total weight; the acid is applied by its spraying to the dross with following drying in the drying chamber with hot air having temperature not more than 50°C. EFFECT: increasing of enhancing degree of the cement stone on retention of rheological properties and setting time of grouting mortars. 1 ex.

Изобретение относится к составу расширяющей добавки к цементу и может быть использовано в промышленности строительных материалов и нефтяной промышленности для получения высокоэффективных вяжущих и тампонажных растворов. Технический результат - увеличение степени расширения цементного камня при сохранении реологических свойств тампонажного раствора и сроков схватывания. Расширяющая добавка к цементу, содержащая шлак переработки вторичного алюминия, содержит указанный шлак состава, мас.%: Al₂O₃ 65-70, AlN₃ 10-15, Al 1-5, NaCl-KCl 10-23, модифицированный органической кислотой в количестве 0,1-1 мас.% по отношению к общей массе добавки распылением ее на указанный шлак крупностью не более 100 мкм, с последующей сушкой в сушильной камере теплым воздухом с температурой не более 50°С.