Микроструктура комплексного кремнийсодержащего модификатора

Abstract

It is shown that the microstructure of the complex silicon-containing modifier Insteel 7.0 is formed by six phases: TiFeSi2, Ca1-x(La, Ce)xSi2, CaSi2, FeSi2, TiCN and a BaSi2-based phase containing Ca, Si, Al, and Mg. Silicides of titanium, iron, calcium, and barium facilitate modifier dissolution due to their low melting points, enhancing the effect of modifying when entering into a liquid metal. Various methods were used to clarify the composition of the phase containing rare earth metals (REM). According to the XRD, this phase has a composition – Ca0.8La0.2Si2, according to the EDX – Ca1-x(La,Ce)xSi2. The REM-containing phase able to reduce the content of dissolved gases (O and N) in the liquid steel after modifier addition. The TiCN particles (Tmelt = 3200 °C) can act as inoculators, i.e. serve as crystallization centers after introduction into the metal melt.

Установлено, что в микроструктуре комплексного кремнийсодержащего модификатора Insteel 7.0 присутствует шесть фаз: TiFeSi2, Ca1-х(La, Ce)хSi2, CaSi2, FeSi2, TiCN и фаза на основе BaSi2, содержащая Ca, Si, Al и Mg. Силициды титана, железа, кальция и бария в составе модификатора благодаря низкой температуре плавления облегчают его растворение, усиливая эффект модифицирования при вводе в жидкий металл. Использование различных методов исследования позволило уточнить состав фазы, содержащей РЗМ. Согласно РСФА эта фаза имеет состав – Ca0,8La0,2Si2, согласно РСМА – Ca1-х(La, Ce)хSi2. Содержащая РЗМ фаза, входящая в состав модификатора, при введении в расплав стали способна снижать содержание растворенных в металле газов (O и N). Частицы фазы TiCN (Тпл. = 3200 °C) могут служить инокуляторами, т.е. выступать в качестве центров кристаллизации после введения в расплав металла.