|Title:||Oxygen content and defect structure of the perovskite La0.5Ba0.5CoO3–δ|
|Authors:||Malyshkin, D. A.|
Novikov, A. Yu.
Tsvetkov, D. S.
|Publisher:||Уральский федеральный университет|
|Citation:||Malyshkin D. A. Oxygen content and defect structure of the perovskite La0.5Ba0.5CoO3–δ / D. A. Malyshkin, A. Yu. Novikov, D. S. Tsvetkov // Chimica Techno Acta. — 2018. — Vol. 5, No. 2. — P. 117–124.|
|Abstract:||Perovskite-type complex oxide La0.5Ba0.5CoO3–δ, promising cathode material for solid oxide fuel cells and precursor for synthesis of double perovskite LaBaCo2O6–δ, was prepared as a single-phase material. Its oxygen content was measured by two independent techniques in the temperature range 1000–1100 °C and at oxygen partial pressures corresponding to the stability field of cubic phase. The defect chemistry of this material was studied using the measured δ = f(pO2, T) dependences. The defect structure model based on the localized nature of the electronic defects was proposed and successfully verified.|
|Origin:||Chimica Techno Acta. 2018. Vol. 5. № 2|
|Appears in Collections:||Chimica Techno Acta|