Please use this identifier to cite or link to this item: http://hdl.handle.net/10995/42677
Title: Определение характеристик распыления электролитического покрытия Ni-P с использованием атомно-эмиссионного спектрометра с тлеющим разрядом GDS 850 A
Other Titles: Sputtering characteristics determination of Ni-P electrolytic coating by glow discharge atomic-emission spectrometer GDS 850 A
Authors: Чичерская, А. Л.
Пупышев, А. А.
Chicherskaya, A. L.
Pupyshev, A. A.
Issue Date: 2014
Publisher: Уральский федеральный университет
Citation: Чичерская А. Л. Определение характеристик распыления электролитического покрытия Ni-P с использованием атомно-эмиссионного спектрометра с тлеющим разрядом GDS 850 A / А. Л. Чичерская, А. А. Пупышев // Аналитика и контроль. — 2014. — № 1. — С. 50-57.
Abstract: Выполнен обзор литературы по послойному анализу покрытий никель-фосфор методом атомно-эмиссионной спектрометрии с тлеющим разрядом. Особое внимание уделено подбору оптимальных значений операционных параметров разряда и способу определения скорости распыления материала. Изготовлены образцы покрытий никель-фосфор путем электролитического нанесения на подложку из сплава 29 НК в ванне химического никелирования. С помощью рентгеновского электронно-зондового микроанализа доказана однородность химического состава покрытий. С использованием атомно-эмиссионного спектрометра с тлеющим разрядом GDS 850 A в режиме постоянного тока на образцах покрытий получены кратеры катодного травления при постоянном давлении газа и различных операционных параметрах разряда (сила тока и напряжение). На механическом профилометре с алмазной иглой проведено изучение формы кратеров в зависимости от операционных условий катодного распыления. Предложен способ численной оценки плоскостности дна кратера, позволяющий подобрать оптимальные условия для послойного анализа покрытия никель-фосфор. Измерены значения скорости распыления сплава методами взвешивания образцов и измерения размеров кратеров. Проведено определение коэффициента распыления материала покрытия относительно сплава 29 НК. Полученные значения скорости и коэффициентов распыления подтверждаются данными, представленными в литературе.
Conducted a review of the literature regarding the determination of cathodic sputtering rate for Ni-P coating and investigation of crater shape produced as a result of result of cathode etching in glow discharge lamp. The values of coating sputtering rate, main methods for determining the sputtering rate and its factors as well as the techniques of investigation into the ion etching crater shape depending on the parameters of the glow discharge were presented. During the research of the sputtering characteristics, the samples of Ni-P electrolytic coating on conducting substrate from 29 NK-alloy were made. Using the X-Ray electron-probe microanalysis the uniformity of chemical composition was studied. By utilizing a glow discharge atomic-emission spectrometer “GDS 850 A” on the coating material the craters were obtained at different values ​​of amperage and DC discharge voltage (gas pressure is constant). Craters were studied by mechanical profilometer with a diamond needle. As a result, a new quantitative method for classifying the deviation from the plane of the bottom of the crater was suggested. Optimum operating conditions for flat-bottomed craters at different operating conditions of the analysis were selected. In addition, the sputtering rate of the coating material was determined by weighing and measuring the volume of the crater. It is noted that the weighing method has significantly higher error and does not take into account the features of the sputtering material. Sputtering rate values that were obtained by using the volume crater method are comparable to the data described in the scientific literature. Defined sputtering rate values for Ni-P coating with respect to the substrate material. These values correlate well with the data presented by the developer of standard samples for the stratified analysis.
Keywords: GLOW DISCHARGE
DIRECT CURRENT
SPUTTERING RATE
NICKEL-PHOSPHORUS
CRATER SHAPE
ATOMIC-EMISSION SPECTROMETRY
АТОМНО-ЭМИССИОННАЯ СПЕКТРОМЕТРИЯ
ТЛЕЮЩИЙ РАЗРЯД ПОСТОЯННОГО ТОКА
СКОРОСТЬ РАСПЫЛЕНИЯ
ФОРМА КРАТЕРА
ГАЛЬВАНИЧЕСКОЕ ПОКРЫТИЕ NI-P
URI: http://hdl.handle.net/10995/42677
RSCI ID: 21232267
ISSN: 2073-1442
DOI: 10.15826/analitika.2014.18.1.005
Origin: Аналитика и контроль. 2014. № 1
Appears in Collections:Аналитика и контроль