Влияние исходной микроструктуры сплавов TNM-В1 и TI-44AL-4(V,NB,ZR)-0.2B-РЗМ на механическое поведение ниже температуры эвтектоидного превращения

Abstract

Effect of initial microstructure on mechanical behavior of TiAl-based alloys has been studied. At high cooling rate in both alloys lamellar microstructure did not form. Heating of this alloys state to temperature below eutectoid transformation led to formation of lamellar structure. However in Ti-44Al-4(V,Nb,Zr)-0.2B-REE it was unstable during soaking. Effect of microstructure differences between alloys on mechanical behavior has been studied. Decrease flow stress after heat treatment Ti-44Al-4(V,Nb,Zr)-0.2B-REE in comparison with TNM-В1 has been shown.

Изучено влияние исходной микроструктуры на механическое поведение двух сплавов на основе γ-TiAl. При высокой скорости охлаждения в обоих сплавах не образуется пластинчатая микроструктура. Последующее нагревание сплава в таком состоянии до температуры ниже эвтектоидной приводит к образованию пластинчатой структуры. Пластинчатая структура сплава Ti-44Al-4(V,Nb,Zr)-0.2B-РЗМ нестабильна и пластины трансформируются в равноосные частицы. Изучено влияние микроструктуры сплавов перед деформацией на механическое поведение при температурах ниже эвтектоидной. Показано снижение напряжений течения, после термической обработки сплава Ti-44Al-4(V,Nb,Zr)-0.2B-РЗМ по сравнению с TNM-В1.