Формирование текстуры молибдена при горячей прокатке и последующем отжиге

Abstract

Texture of molybdenum’s sheet after hot rolling 90% and temperature 1100 °C throughout the thickness consists of the set of the stable orientations (001)[110], {112}<110>, {111}<112>. During recrystallization at 1200 °C orientation {001}<110> is weakened, the other orientations are enhanced. It is shown that the orientations of recrystallized grains are connected with the orientations of deformed grains by rotations at defined angles about axes <110>.The formation of recrystallization texture can be explained by the movement of special boundaries Σ9, Σ11. They appeared after the occurrence of relevant special misorientations between the components of the deformation texture.

Текстура молибденового листа после горячей прокатки при температуре 1100 °С с суммарной степенью деформации, превышающей 90 %, по всей толщине состоит из набора стабильных ориентировок: (001)[110], {112}<110>, {111}<112>. В процессе рекристаллизации при 1200 °С ориентировка {001}<110> ослабляется, остальные ориентировки усиливаются. Показано, что ориентировки рекристаллизованных зерен с ориентировками деформированных зерен связаны поворотами на определенные углы вокруг осей <110>. Формирование текстуры рекристаллизации может быть объяснено движением специальных границ типа Σ9, Σ11, появлению которых предшествовало образование соответствующих специальных разориентаций между компонентами деформационной текстуры.