Synthesis and investigation of La1–xBixMn1–yFeyO3–δ structure

Abstract

Doped lanthanum manganites La1-xBixMn1-yFeyO3-δ(x=0.0-0.3; у=0.0-0.5, Δх, у=0.1) with perovskite-like structure were synthesized by solid state reaction and solution method. It was determined by X-ray diffraction that sintered samples have rhombohedral symmetry (S.G. R-3c). The parameters of unit cell were calculated. The morphology of briket was investigated by scanning electron microscopy. It was found that sintered sample is homogeneous, porous and grains are formed by different size. Elemental composition was checked by atomic emission spectroscopy. Additional studies were performed by TG/DSC and laser diffraction (analysis of particle size distribution).

Проведен синтез перовскитоподобных соединений на основе манганита лантана La1-xBixMn1-yFeyO3-δ (x = 0,0-0,3; у = 0,0-0,5, Δх, у = 0,1). Методом рентгенофазового анализа определено, что образцы обладают ромбоэдрической структурой (Пр. гр. R-3c). Рассчитаны параметры элементарных ячеек, построены их концентрационные зависимости. Проведено исследование размера частиц по размерам. Изучена морфология поверхности и выполнен энергодисперсионный микроанализ. Химический состав образцов определен с помощью атомно-эмиссионной спектроскопии с индуктивно-связанной плазмой (АЭС-ИСП). Найденный элементный состав соответствует значениям, заявленным в формуле. ТГ/ДСК исследования показали убыль массы (~1 %) при температурах выше 750 °С.