Механизм формирования пленок SnS химическим осаждением из водных растворов

Abstract

The results of investigation of the growth mechanism of SnS thin films prepared by hydrochemical deposition by means of a scanning probe microscopy are presented. According to the results of a comparative analysis of layers morphology at different growth stages and the use of fractal formalism growth model of SnS films by clustercluster aggregation with elements of self-organization is proposed. It is shown that there is a solid layer, which again are deposited particles of the solution. The process has expressed periodic self-organizing nature. The study showed that the proposed model of film growth SnS when hydrochemical deposition agrees well with experiments and proves difficult coagulation mechanism of the formation of hard phase of the satu-rated aqueous solution.

В работе представлены результаты исследования механизма роста пленок сульфида олова при химическом осаждении из водных растворов с использованием сканирующей зондовой микроскопии. По результатам сравнительного анализа морфологии слоев на различных этапах роста и использования фрактального формализма предложена модель роста пленок SnS путем кластер-кластерной агрегации с элементами самоорганизации. Показано, что формируется сплошной слой, на котором снова осаждаются микрочастицы из раствора. Процесс имеет выраженный периодический самоорганизующийся характер. Проведенное исследование показало, что предложенная модель роста пленок SnS при гидрохимическом осаждении хорошо согласуется с экспериментами и доказывает сложный агрегативный механизм формирования твердой фазы из пересыщенного водного раствора.