Определение растворимости хлоридов переходных d-элементов в хлоралюминатных расплавах

Abstract

Solubility of several transition metal chlorides (NiCl2, CrCl2, MoCl3, FeCl2) was measured in KCl-AlCl3 based melts. It was found that the solubility of studied metal chlorides depends on K : Al mole ratio. MoCl3 solubility decreases with increasing AlCl3 content. Solubility of CrCl2 and FeCl2 reaches maximum at K : Al ratio of 1 and decreases when this ratio either de-creases or increases. The dependence of NiCl2 solubility on K : Al mole ratio is V-shaped with the maximum near 0.9–0.95. The effect of temperature on solubility of transition metal chlorides in KCl-AlCl3 melts was also investigated. Increasing temperature does not alter the character of «solubility – K : Al mole ratio» dependences.

Представлены результаты выполненных исследований по определению растворимости в расплавах на основе KCl-AlCl3 хлоридных соединений ряда переходных d-элементов (Ni, Cr, Mo, Fe). Изучено влияние мольного отношения KCl : AlCl3 и температуры на растворимость хлоридов исследуемых металлов в хлоралюминатных расплавах. Показано, что растворимость хлорида молибдена в расплавах KCl-AlCl3 снижается по мере обогащения расплава по AlCl3 (иногда величина растворимости уменьшается на порядок). Растворимость хлорида никеля имеет V-образную зависимость от мольного отношения K : Al с минимумом в области мольных отношений K : Al несколько ниже единицы. Разница в растворимости NiCl2 в расплавах различного состава может достигать двух порядков. Растворимость хлоридов хрома и железа, наоборот, имеет максимум в области эквимолярного состава KCl-AlCl3, снижаясь как при увеличении, так и при уменьшении мольного отношения K : Al.